Potential influence of microorganisms on the corrosion of carbon steel in the French high- and intermediate-level long-lived radioactive waste disposal context

In the context of the high-level radioactive waste disposal CIGEO, the corrosion rate due to microbially influenced corrosion (MIC) has to be evaluated. In France, it is envisaged to dispose of high- and intermediate-level long-lived radioactive waste at a depth of 500 m in a deep geological disposal, drilled in the Callovo-Oxfordian claystone (Cox) formation. To do so, a carbon steel casing will be inserted inside disposal cells, which are horizontal tunnels drilled in the Cox. A specific cement grout will be injected between the carbon steel casing and the claystone. A study was conducted to evaluate the possibility of MIC on carbon steel in the foreseeable high radioactive waste disposal. The corrosiveness of various environments was investigated at 50°C and 80°C with or without microorganisms enriched from samples of Andra's underground research laboratory. The monitoring of corrosion during the experiments was ensured using gravimetric method and real-time corrosion monitoring using sensors based on the measurements of the electrical resistance. The corrosion data were completed with microbiological analyses including cultural and molecular characterizations.     

Corrosion behavior of T24, T92, VM12, and AISI 304 steels exposed to KCl–NaCl–K2SO4–Na2SO4 salt mixtures

The corrosion mechanisms of T24, T92, VM12, and AISI 304 steels are studied under the influence of NaCl–KCl, NaCl–Na₂SO₄, and KCl–K₂SO₄ salt mixtures in a dry air atmosphere at 650°C for 15 days. NaCl–KCl was the most aggressive deposit and AISI 304 stainless steel exhibited the highest corrosion resistance. There was no relation between the Cr content of the ferritic steels and their corrosion resistance in NaCl–KCl. In contrast, the resistance of high-Cr steels was better when exposed to NaCl–Na₂SO₄ and KCl–K₂SO₄. The high-Cr and the low-Cr steels were more susceptible to NaCl–Na₂SO₄ and to KCl–K₂SO₄, respectively.     

Farmers' preferences for adopting on-farm concentration of raw milk: Results from a discrete choice experiment in Germany

Milk concentrates are used in the manufacturing of dairy products such as yogurt and cheese or are processed into milk powder. Processes for the nonthermal separation of water and valuable milk ingredients are becoming increasingly widespread at farm level. The technical barriers to using farm-manufactured milk concentrate in dairies are minimal, hence the suspicion that the practice of on-farm raw milk concentration is still fairly uncommon for economic reasons. This study, therefore, set out to investigate farmers' potential willingness to adopt a raw milk concentration plant. The empirical analysis was based on discrete choice experiments with 75 German dairy farmers to identify preferences and the possible adoption of on-farm raw milk concentration. The results showed that, in particular, farmers who deemed the current milk price to be insufficient viewed on-farm concentration using membrane technology as an option for diversifying their milk sales. We found no indication that adoption would be impeded by a lack of trustworthy information on milk processing technologies or capital.     

干熄焦锅炉炉管失效机理分析

通过对干熄焦锅炉炉管及腐蚀产物开展系统研究，提出炉管失效原因为氧化/硫腐蚀＋高温粉尘冲刷。长寿命炉管仅耐磨层发生了较为严重的氧化及硫腐蚀，而近基体层发生了轻微氧化及硫腐蚀，基体只发生了轻微氧化；短寿命炉管耐磨层、近基体层以及基体裂纹内均发生了较为严重的氧化及硫腐蚀，且存在珠光体球化、内表面产生全脱碳层等缺陷。推测短寿命炉管存在超温现象，而超温可加剧氧化及硫腐蚀反应。此外，短寿命炉管遭受了较为严重的高温粉尘冲刷，不仅可造成炉管减薄，还会导致炉管表面温度升高。因此，减少循环气体中粉尘量尤其是大颗粒，可有效减弱冲刷以及控制炉管表面温度，是提高炉管使用寿命的关键。     

An exploration of corrosion inhibition of mild steel in sulphuric acid solution through experimental study and Monte Carlo simulations

Abstract

4-[4-(1H-imidazol-1-yl)methyl)-1H-1,2,3-triazol-1-yl]methylbenzophenone (ITBP) and 4[4-(1H-1,2,4-triazol-1-yl)methyl)-1H-1,2,3-triazol-1-yl]methylbenzophenone (TTBP) are synthesized as new heterocyclic compounds of the triazole derivative family and tested successfully as potential inhibitors for MS in 1?M H₂SO₄ corrosive medium by using gravimetric analysis, electrochemical impedance spectroscopy, potentiodynamic polarization, and energy dispersive X-ray spectroscopy (EDX). Polarization curves show that the tested inhibitors are mixed-type inhibitors. Scanning electron microscopy (SEM) affirmed the existence of an adsorbed film on the steel surface. Monte Carlo simulations were in excellent agreement with the experimental tests.

Abbreviation: PDP: Potentiodynamic Polarization; EIS: Electrochemical impedance spectroscopy; DFT: Density functional theory; MC: Monte Carlo     

变形铝合金表面锆基化学转化膜的研究现状

化学转化膜是金属表面主要的处理方法之一，具备良好的附着力和耐蚀性，能为铝合金提供一定的临时防护。传统的六价铬酸盐化学转化膜在日渐严苛的环保压力下已经逐渐淘汰，取而代之的是近几年发展迅猛的三价铬及无铬锆基化学转化膜。铝合金可分为铸造铝合金和变形铝合金，按照所含主要合金元素和热处理状态可分为若干个系列和型号。本文选取几种典型的变形铝合金，综述了不同铝合金微观组织对转化膜成膜过程的影响，化学转化液添加剂、预处理和后处理工艺对转化膜性能的调控及作用机理，以及几种典型商业钝化剂在变形铝合金表面的应用。总结了目前变形铝合金表面锆基化学转化膜仍面临的问题和发展趋势，未来化学转化膜需在满足新型铝合金发展要求的基础上，通过不同有机、无机添加剂以及外场作用对转化膜的成膜均一性、完整性进行调控，以提高转化膜的综合性能。     

Behavior of 316L stainless steel containing corrosion pits under cyclic loading

The environmental performance of 316L grade stainless steel, in the form of tensile specimens containing a single corrosion pit with various aspect ratios, under cyclic loading in aerated chloride solutions is investigated in this study. Results from environmental tests were compared and contrasted with those obtained using finite element analysis (FEA). Fractography of the failed specimens obtained from experiments revealed that fatigue crack initiation took place at the base of the shallow pit. The crack initiation shifted towards the shoulder and the mouth of the pit for pits of increasing depth. This process is well predicted by FEA, as the strain contour maps show that strain is the highest around the centric strip of the pit. However, for shallow pits, local strain is uniformly distributed around that strip but begins to concentrate more towards the shoulder and the mouth region for increasingly deep pits.